The objective of the present investigation was to clarify the influence of raw material on the quantity, and especially quality of rotary cut birch veneer by running cutting tests with constant tool setting under factory conditions and with bolts of normal size. The quality of the veneer was mainly examined in laboratory.
The result showed that with an increase in bolt size the yield increases and reaches the maximal value in the diameter range of 251–275 mm and 226–250 mm for 60-inch and 50-inch bolt, respectively. With a decrease in bolt length the yield becomes higher. With the increase in the bolt size the quality of the veneer improves.
Defects in the shape of the bolt, such as crookedness, taper and oval form, decrease the yield. The good quality of the bolts affects most the yield of full-size sheets. Increase of knottiness decreases the yield by 4–5%. Lowering of the bolt temperature below 0 °C causes a sharp decline in the yield. Moisture content of the wood did not markedly affect the yield, but it improved the quality of the veneer. The minimum moisture content was 75%.
For the technical quality of the veneer, bolt temperature was the most decisive raw material factor. Also shape defects, of which crookedness was most serious, decreased the technical quality. Increase in summerwood percentage improved the quality.
The PDF includes a summary in English.
-